It is made of high-quality aluminum plate lamination, and the surface layer adopts spray and roller coating processes.
It has excellent weight, strength, earthquake resistance and other effects, and has good weather resistance and corrosion resistance. The double-layer lamination process can ensure good surface smoothness.
Fireproof and high temperature resistant, with excellent fireproof performance, effective high temperature resistance, and not easy to change after long-term use.
It is made of high-quality aluminum plate lamination, and the surface layer adopts spray and roller coating processes.
It has excellent weight, strength, earthquake resistance and other effects, and has good weather resistance and corrosion resistance. The double-layer lamination process can ensure good surface smoothness.
Fireproof and high temperature resistant, with excellent fireproof performance, effective high temperature resistance, and not easy to change after long-term use.
Product Description
Detail Shows
Install node graph
Performance Parameters
| Test items | Standard requirement | Test result | Single conclusion | According to the standard | |
| Combustion performance level A (A2-s1, d0, t0) | Calorific value of main components (aluminum plate) | ≤3.0MJ/kg | 0MJ/kg | Conform to | GB/T 14402-2007 |
| Calorific value of main components (aluminum honeycomb) | ≤3.0MJ/kg | 0MJ/kg | Conform to | ||
| Calorific value of external secondary components (coating) | ≤4.0MJ/㎡ | 0.8MJ/㎡ | Conform to | ||
| Calorific value of internal secondary components (resin glue) | ≤4.0MJ/㎡ | 3MJ/㎡ | Conform to | ||
| Total heat of combustion | ≤3.0MJ/kg | 1.1MJ/kg | Conform to | ||
| Flame spreads laterally | Did not reach test long wing edge | Did not reach test long wing edge | Conform to | GB/T 20284-2006 | |
| Total smoke production within 600 seconds | ≤50㎡ | 36m2 | Conform to | ||
| Smoke generation rate index | ≤30m2/s2 | 1m2/s2 | Conform to | ||
| Combustion drippings/particles | No burning droplets within 600s | Conform to | |||
| Total heat release in 600s | ≤7.5MJ | 1.2MJ | Conform to | ||
| Burning rate growth index (FIGRA0.2MJ) | ≤120W/s | 12W/s | Conform to | ||
| Smoke toxicity | Achieve quasi-safety level ZA1 | Achieve quasi-safety level ZA1 | Conform to | GB/T 20285-2006 | |
| Combustion sample installation instructions | 1. The specimen shall be installed in accordance with Article 5.2.2b) of GB/T20284-2006. 2. The back plate of the sample is a calcium silicate plate with a thickness of 12mm and a density of 800kg/m². 3. The fire-receiving surface of the sample is the decorative surface. |
||||
About Us
FSILON was founded in 2005. A leading prefabricated interior demonstration enterprise in China, listed on the main board of China A shares on August 3, 2020.
We are a one-step building materials enterprise that covers home decoration, engineering and commercial chain decoration. Our company provides R&D, production, manufacturing, sales, and gpod services. We are located in Haiyan, Zhejiang, China, with 260,000 square meters of super-large smart home industrial park.
As manufacturing sector expands globally, FSILON has seized new opportunities. By capitalizing on the advancements and industrial resources of home building materials industry, FSILON has established the FSL home building materials supply chain platform. This platform aims to offer overseas customers a one-stop-shop for sourcing and supplying home building materials, along with modular and turnkey solutions.
At present, FSL home building materials supply chain industry platform has provided business for customers from the United States, Bangladesh, Angola, Vietnam, Dubai, Zambilai and other countries and regions.
Capicity of Production
Related Products